    3. Round Rod in PVC U 2000 mm green
    Standard
    Round Rod in PVC U 2000 mm green
    Round Rod in PVC U 2000 mm green
    PE round bar

    Round Rod in PVC U 2000 mm green

    Item no. P1201103
    Tillgängligt från lager
    • Outer diameter

    The selected combination does not exist.

    PVC U is rigid, unplasticized polyvinyl chloride with good chemical resistance, intended for turned and milled parts in a chemical environment. The material is stiff, dimensionally stable and easy to machine.

    The green round rod is 2000 mm long and suits turned parts in a chemically exposed environment. We cut it to the length you need.

    Technical specifications

    Format
    Rundstång
    Benefits
    Chemical Resistant

    God motståndskraft mot kemikalier, syror och baser

    Dimensionally Stable

    Låg krypning och minimal formförändring

    Easy to Machine

    Lätt att bearbeta med konventionella verktyg

    Electrically Insulating

    Hög volym- och ytresistivitet

    Flame Retardant

    Uppfyller brandklassning V-0 eller bättre

    High Stiffness

    Hög elasticitetsmodul och formstabilitet

    Low Water Absorption

    Minimal fuktupptagning, dimensionsstabil

    Weldable

    Kan sammanfogas genom svetsning

    Machining
    Bonding

    Sammanfogning med lim

    CNC Machining

    Datorstödd bearbetning

    Drilling

    Håltagning med borr

    Milling

    Bearbetning med fräs

    Sawing

    Kapning med såg (band-, cirkelsåg)

    Threading

    Skärning av gängor (invändig/utvändig)

    Turning

    Bearbetning i svarv

    Welding

    Sammanfogning genom svetsning (varmgas, spegel, ultraljud)

    Property Value Unit Test standard
    Density & Weight
    Density > 1,37 g/cm³ ISO 1183
    Impact Resistance
    Charpy Notched Impact Strength > 2 kJ/m² ISO 179
    Tensile Modulus of Elasticity 3325 MPa ISO 527
    Yield Stress 57 MPa ISO 527
    Strain at Yield 4 % ISO 527
    Tensile Strain at Break > 14 % ISO 527
    Tensile Stress at Break 40 MPa ISO 527
    Flexural Strength 90 MPa ISO 178
    Shore D Hardness 82 Shore D ISO 868
    Vicat Softening Temperature (VST/B/50) 75 °C ISO 306
    Max. Continuous Service Temperature 60 °C UL746B
    Moisture absorption (23°C/50% RH) 0,2 % ISO 62
    Water Absorption to Saturation 0,5 % ISO 62
    Coefficient of Linear Thermal Expansion 75 x 10⁻⁶ 1/K ISO 11359-2
    Surface Resistivity > 10¹³ Ω EN 61340
    Dielectric Strength 39 kV/mm IEC 60243-1
    Flammability Rating (UL 94) V-0 from 1 mm UL 94
    Fire Classification Building (DIN 4102/EN 13501) B1 per DIN 4102, B-s3,d0 per EN 13501

    Värdena ovan är genomsnitt från statistiska tester som görs löpande. De anges som information och är inte bindande, om inte annat uttryckligen avtalats i ordererkännandet. För batchspecifika värden kan PlastShop tillhandahålla ett EN 10204-2.2-certifikat.