Round Rod in PA6 C GL 1000 mm black
Variants
| Item no. |
|---|
| Loading variants ... |
This is a round rod made of PA6 C GL, glide optimized cast polyamide 6, dry lubricated with a solid lubricant.
The material is semi-crystalline and has a melting point of 218 °C.
The density is 1.13 g/cm³, the yield strength 76 MPa and the tensile modulus 3200 MPa.
The elongation at break is 18 percent, Shore D 79 and the unnotched impact strength gives no break.
The continuous service temperature is 100 °C, 130 °C for short periods. The fire rating is HB.
Used for bearing bushings, slide strips, chain guides, wear rails and other sliding surfaces that have to run dry without regular relubrication.
The rod can be turned, milled, drilled and tapped with tools meant for engineering plastics. Carbide and coated inserts work best. Moisture affects the dimensions, so let the material rest in the workshop climate before the finishing cuts.
This particular round rod in PA6 C GL measuring 1000 mm in the color black suits dry sliding surfaces such as bearing bushings, slide strips and wear rails without regular lubrication.
Not sure whether the material suits your case? Get in touch with us.
Technical specifications
Machining
Datorstödd bearbetning
Håltagning med borr
Bearbetning med fräs
Kapning med såg (band-, cirkelsåg)
Bearbetning i svarv
| Property | Value | Unit | Test standard |
|---|---|---|---|
| Density & Weight | |||
| Density | 1,13 | g/cm³ | ISO 1183 |
| Moisture Absorption | |||
| Water Absorption to Saturation | 0,3 | % | ISO 62 |
| Tensile Properties | |||
| Yield Stress | 76 | MPa | ISO 527-2 |
| Tensile Modulus of Elasticity | 3200 | MPa | ISO 527-2 |
| Strain at Yield | 14 | % | ISO 527-2 |
| Tensile Strain at Break | 18 | % | ISO 527-2 |
| Flexural Properties | |||
| Flexural Strength | 103 | MPa | ISO 178 |
| Flexural Modulus of Elasticity | 3100 | MPa | ISO 178 |
| Impact Resistance | |||
| Charpy Notched Impact Strength | 4 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | Utan brott | kJ/m² | ISO 179 |
| Hardness | |||
| Shore D Hardness | 79 | Shore D | DIN EN ISO 868 |
| Ball Indentation Hardness | 159 | MPa | ISO 2039-1 |
| Compressive Properties | |||
| Compressive Strength | 75 | MPa | ISO 604 |
| Compressive Modulus | 2500 | MPa | ISO 604 |
| Temperature Limits | |||
| Melting Point | 218 | °C | ISO 3146 |
| Max. Service Temperature (short-term) | 130 | °C | |
| Max. Continuous Service Temperature | 100 | °C | |
| Heat Deflection Temperature (HDT/A) | 90 | °C | DIN EN ISO 75 |
| Glass Transition Temperature | 45 | °C | DIN EN ISO 11357 |
| Thermal Conductivity | |||
| Specific Heat Capacity | 1,7 | kJ/(kg·K) | |
| Thermal Conductivity | 0,38 | W/(m·K) | DIN 52612 |
| Thermal Expansion | |||
| Coefficient of Linear Thermal Expansion | 115 x 10⁻⁶ | ISO 11359-2 | |
| Insulation Properties | |||
| Dielectric Strength | 20 | kV/mm | IEC 60243-1 |
| Volume Resistivity | 10¹⁴ | Ω·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3,7 | IEC 60250 | |
| Static Dissipation | |||
| Surface Resistivity | 10¹⁴ | Ω | DIN EN 62631-3-2 |
| Comparative Tracking Index (CTI) | 600 | V | IEC 60112 |
| Flammability Rating | |||
| Flammability Rating (UL 94) | HB | UL 94 | |
Värdena ovan är genomsnitt från statistiska tester som görs löpande. De anges som information och är inte bindande, om inte annat uttryckligen avtalats i ordererkännandet. För batchspecifika värden kan PlastShop tillhandahålla ett EN 10204-2.2-certifikat.
Documents available for download: