    Round Rod in PA6 C MoS² 3000 mm black
    Round Rod in PA6 C MoS² 3000 mm black
    PA round bar

    Round Rod in PA6 C MoS² 3000 mm black

    Tillgängligt från lager
    • Outer diameter

    The selected combination does not exist.

    Variants

    Item no.
    Loading variants ...

    This is a round rod made of PA6 C MoS², cast polyamide 6 with molybdenum disulfide added as a dry lubricant.

    The material is semi-crystalline and has a melting point of 219 °C.

    The density is 1.15 g/cm³, the yield strength 81 MPa and the elongation at break 48 percent.

    The tensile modulus is 3200 MPa and the sliding friction against steel 0.32 dry.

    The continuous service temperature is 103 °C, 165 °C for short periods and the lowest working temperature -40 °C. The fire rating is HB.

    Used for bearing bushings, slide strips, chain guides, wear rails and other sliding surfaces that have to run dry without regular relubrication.

    The rod can be turned, milled, drilled and tapped with tools meant for engineering plastics. Carbide and coated inserts work best. Moisture affects the dimensions, so let the material rest in the workshop climate before the finishing cuts.

    This particular round rod in PA6 C MoS² measuring 3000 mm in the color black suits dry sliding surfaces such as bearing bushings, slide strips and wear rails without regular lubrication.

    Not sure whether the material suits your case? Get in touch with us.

    Technical specifications

    Format
    Rundstång
    Additives
    Molybdenum Disulfide (MoS₂)
    Property Value Unit Test standard
    Density & Weight
    Density 1,15 g/cm³ ISO 1183
    Tensile Properties
    Yield Stress 81 MPa ISO 527-2
    Tensile Modulus of Elasticity 3200 MPa ISO 527-2
    Tensile Strain at Break 48 % ISO 527-2
    Flexural Properties
    Flexural Strength 116 MPa ISO 178
    Flexural Modulus of Elasticity 3150 MPa ISO 178
    Impact Resistance
    Charpy Notched Impact Strength 4 kJ/m² ISO 179
    Charpy Unnotched Impact Strength Utan brott kJ/m² ISO 179
    Hardness
    Shore D Hardness 83 Shore D Shore D
    Ball Indentation Hardness 150 MPa ISO 2039-1
    Compressive Properties
    Compressive Modulus 2800 MPa ISO 604
    Temperature Limits
    Melting Point 219 °C ISO 3146
    Max. Service Temperature (short-term) 165 °C
    Max. Continuous Service Temperature 103 °C
    Minimum temperature -40 Grader Celsius
    Glass Transition Temperature 43 °C ISO 3146
    Thermal Conductivity
    Thermal Conductivity 0,28 W/(m·K) DIN 52612
    Thermal Expansion
    Coefficient of Linear Thermal Expansion 93 x 10⁻⁶ ISO 11359-2
    Static Dissipation
    Surface Resistivity 10¹⁴ IEC 60093
    Comparative Tracking Index (CTI) 600 V IEC 60112
    Flammability Rating
    Flammability Rating (UL 94) HB UL 94

    Värdena ovan är genomsnitt från statistiska tester som görs löpande. De anges som information och är inte bindande, om inte annat uttryckligen avtalats i ordererkännandet. För batchspecifika värden kan PlastShop tillhandahålla ett EN 10204-2.2-certifikat.